PHiLARC Products
- Carbon Steel Electrodes
- High Tensile Strength Steel
- For Low Temperature Steel
- Heat Resisting Steel Electrodes
- Atmospheric Corrosion Resisting
- Hardfacing Electrodes
- Stainless Steel Electrodes
- Nickel and Nickel Alloy Electrodes
- Cast Iron Electrodes
- Aluminum Alloy Electrodes
- Bronze and Copper Alloy Electrodes
- Gouging and Cutting Electrodes
- Solid Welding Wire (GMAW and GTAW)
- Oxy Fuel Gas Filler Rods for Brazing
- Oxy Fuel Gas Brazing FLuxes
- Submerged Arc Weding Wire and Flux
- Flux Cored Wires (FCAW)
PHILHARD 7200
AWS Specification :AWS A5.13 E FeMn-A
JIS Specification : NONE
Other Specification : DIN 8555: E 7-UM-250-KP
I. APPLICATIONS:
The main application areas are the building industry, quarries and mines for surfacing worn high Mn steel parts e.g. excavator pins, buckets and teeth, mill hammers, crusher jaws, cones and beaters, impeller bars, railway building machinery, shunts, heart and cross pieces.
II. DESCRIPTION:
PHILHARD 7200 is predominantly suited for tough and crack resistant joinings and surfacings on parts of high Mn-steel subject to extreme impact, compression and shock. Buildups on C-steel are also possible.
The High Mn-content produces a fully austenitic deposit. The deposit is highly workhardening and hardens during service from originally 200-250 HB to 450 HB. Machining is possible with tungstene carbide tools.
III. NOTES ON USAGE:
Hold electrode as vertically as possible. Welding should be done at low temperature. Interpass temperature should not exceed 250° C. It is therefore recommended to weld short beads and to allow for continuous cooling during welding or to place the workpiece in a cold water bath with only the welding area sticking out of water.
IV. TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%):
C |
Si |
Mn |
Cr |
Mo |
Ni |
0.70 |
0.27 |
13.00 |
4.50 |
0.53 |
4.00 |
V. HARDNESS OF WELD METAL:
Hardness, as welded, 3 layers weld metal 95 - 100 HRB (220 – 260 Hv)
work hardened 43 – 45 HRC (420 – 450 Hv)
VI. WELDING POSITIONS: FLAT, VERTICAL UP, OVERHEAD
VII. SIZES AVAILABLE AND RECOMMENDED CURRENTS (AC or DC + ):
Electrodes |
Ø mm x L |
3.2 x 350 |
4.0 x 350 |
5.0 x 350 |
Amperage |
A |
110-140 |
150-180 |
180-210 |