PHiLARC Products
- Carbon Steel Electrodes
- High Tensile Strength Steel
- For Low Temperature Steel
- Heat Resisting Steel Electrodes
- Atmospheric Corrosion Resisting
- Hardfacing Electrodes
- Stainless Steel Electrodes
- Nickel and Nickel Alloy Electrodes
- Cast Iron Electrodes
- Aluminum Alloy Electrodes
- Bronze and Copper Alloy Electrodes
- Gouging and Cutting Electrodes
- Solid Welding Wire (GMAW and GTAW)
- Oxy Fuel Gas Filler Rods for Brazing
- Oxy Fuel Gas Brazing FLuxes
- Submerged Arc Weding Wire and Flux
- Flux Cored Wires (FCAW)
PTS-420
AWS Specification; AWS A5.9 ER 420
I. APPLICATIONS:
For surfacing of overlays having good abrasion resistance in combination with scaling resistance. e.g. exhaust gas systems, rollers and valve faces.
II. TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%):
C |
Si |
Mn |
Cr |
Ni |
Mo |
0.28 |
0.38 |
0.43 |
13.12 |
0.40 |
0.14 |
III. TYPICAL MECHANICAL PROPERTIES OF WELD METAL : AT 850° C x 2 hrs
Tensile Strength N/mm2 (Ksi) |
Yield Point N/mm2 (Ksi) |
Elongation % |
Hardness (as welded) HRC |
980 (142) |
860 (125) |
45 |
49-52 |
IV. SIZES AVAILABLE :
Dia.(mm) |
1.6 |
2.0 |
2.4 |
3.2 |
4.0 |
Length (mm) |
1000 |
1000 |
1000 |
1000 |
1000 |
Unit wt./packing (kgs.) |
5.0 |
5.0 |
5.0 |
5.0 |
5.0 |
TEST RESULT
The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.