PHILHARD KH-10CR

DIN 8555: E6-UM-55-GP

DESCRIPTION:

PHILHARD KH-10CR is a rutile coated surfacing electrodes against metal to metal wear. It offers a combination of abrasions, adhesion and impact resistance up to 500°C.

APPLICATIONS:

Typical applications are bucket teeth and blades, slides, conveyor screws, mixer parts, gear wheels, crusher hammers, dredge part.

INSTRUCTIONS FOR WELDING:

Generally,a preheat and inter pass temperature of about 200°C is recommended for most applications.

TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%):

C	Si	Mn	Cr
0.66	0.58	0.60	10.68

HARDNESS OF WELD METAL: 54-58 HRC

SIZES AVAILABLE AND RECOMMENDED CURRENTS (AC or DC + ):

Size

(mm)

Dia.

3.2

4.0

5.0

Length

350

Current Range

90~130

130~180

180~230

TEST RESULT

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.