- Heat Resisting Steel Electrodes - PA-10016-D2

PHiLARC Products

Certification of Quality

PA-10016-D2

AWS Specification: AWS A5.5 E10016-D2

JIS Specification: NONE

Other Specification: NONE

I. APPLICATIONS:

The PA-10016-D2 is designed for applications requiring at least 100,000 psi tensile strength, good ductility and crack resistance. Typical applications include manganese-moly castings, alloy forgings, structurals and pressure vessels applications in either the as welded or stress relieved conditions.

II. DESCRIPTIONS:

PA-10016-D2 is a high quality electrode designed for high tensile steels and manganese-molybdenum steels. The coating is specially formulated to resist moisture pick-up under conditions of high heat and humidity. This electrode offers resistance to moisture reabsorption which helps prevent hydrogen cracking and aids in the elimination of starting porosity. Definitely an electrode with high operator appeal.

III. NOTES ON USAGE:

Dry the electrodes at 350-400°C for about one hour before use and store the electrodes at 100-150°C after drying them with attention to keep away from moisture.

Adopt back step method or strike the arc on a small steel plate prepared for this particular purpose, because arc striking on base metal is in danger of initiating cracking.

Keep the arc as short as possible.

Preheat at 100-150°C. The temperature to be applied varies in accordance with plate thickness and kind of steel to be welded.

Pay attention not to exceed proper heat-input because excessive heat-input causes deterioration of impact values and yield strength of weld metal.

IV. TYPICAL CHEMICAL COMPOSITION OF WELD METAL (%):

C	Si	Mn	Mo
0.12	0.41	1.96	0.39

V. TYPICAL MECHANICAL PROPERTIES OF WELD METAL:

Tensile Strength N/mm²(Ksi)

Yield Point N/mm²

(Ksi)

Elongation %

PWHT

735 (107)

630 (91)

620°C x 1 hr

VI. WELDING POSITIONS: ALL POSITIONS

VII. SIZE AND RECOMMENDED CURRENT RANGE (AC or DC +):

Diameter (mm)		2.5	3.2	4.0	5.0
Length (mm)		350	350	400	400
Ampere	Flat	55 - 85	90 - 130	140 - 190	190 - 240
Ampere	V & OH	50 - 80	75 - 115	100 - 160

TEST RESULT

The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.