PHiLARC - The No. 1 Choice of Welders

GALVAWELD

AWS Specification: AWS A5.1 E6019

JIS Specification: Z3211 D4301

Other Specification:

 

I. APPLICATIONS:

  • The low Silicon weld metal deposit of GALVAWELD is specifically designed for the welding of mild steel & plate (Lyco Plate) used in the fabrication of galvanizing baths. By far the greatest threat to long galvanising bath life is Silicon. Higher Silicon levels in the welded joints will result in preferential attack of the joints and a reduction in the life of the bath.

  • The excellent operator appeal of GALVAWELD makes it suitable for a multitude of other applications including the butt and fillet welding of heavy structures, machine frames and pressure vessels.

II. DESCRIPTIONS:

  • Low Silicon Weld Deposit for Welding Galvanizing baths.

  • Can weld all-position (except vertical-down)

  • Weld deposits are highly crack resistant, porosity free and pass radiographic (X-Ray) test-thus very good for mild steel & heavy structural steels.

III. TYPICAL CHEMICAL PROPERTIES OF ALL WELD METAL DEPOSIT(%):

C

Si

Mn

P

S

0.09

0.08

0.61

0.013

0.007

IV. TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL DEPOSIT:

Yield Point

N/mm2 (ksi)

Tensile Strength

N/mm2 (ksi)

Elongation

%

Impact Value

°C, J (°F, Ft-Lbs)

420 (61)

470 (68)

31

-18°, 90 (0°, 66)

V. WELDING POSITIONS : ALL POSITIONS

VI. SIZE & RECOMMENDED CURRENT RANGE: AC or DC (+)

DIAMETER (mm)

2.6

3.2

4.0

5.0

LENGTH (mm)

350

350

400

400

CURRENT

A

F

50-85

80-130

120-180

170-250

V,OH

40-80

60-110

100-150

130-200

                                                 
 
TEST RESULT
The information contained or otherwise referenced herein is presented only as “typical” without guarantee or warranty, and Industrial Welding Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.